Search results for " mgb2"

Proprietà e applicazioni a microonde del MgB2

2008

Depinning frequency in a heavily neutron-irradiated MgB2 sample

2008

The magnetic-field-induced variations of the microwave surface resistance have been investigated in a heavily neutron-irradiated MgB2 sample, in which the irradiation has caused the merging of the two gaps into a single value. The experimental results have been analyzed in the framework of the Coffey and Clem model. By fitting the experimental data, we have determined the field dependence of the depinning frequency, omega_0, at different values of the temperature. Although the pinning is not particularly effective, the value of omega_0 obtained at low temperatures is considerably higher than that observed in conventional low-temperature superconductors.

Microwave surface resistance of pristine and neutron-irradiated MgB2 samples in magnetic field

2008

We report on the microwave surface resistance of two polycrystalline Mg11B2 samples; one consists of pristine material, the other has been irradiated at very high neutron fluence. It has already been reported that in the strongly irradiated sample the two gaps merge into a single value. The mw surface resistance has been measured in the linear regime as a function of the temperature and the DC magnetic field, at increasing and decreasing fields. The results obtained in the strongly irradiated sample are quite well justified in the framework of a generalized Coffey and Clem model, in which we take into account the field distribution inside the sample due to the critical state. The results ob…

Local tunneling study of three-dimensional order parameter in the pi band of Al-doped MgB2 single crystals

2007

We have performed local tunneling spectroscopy on high quality Mg$_{1-x}$Al$_x$B$_2$ single crystals by means of Variable Temperature Scanning Tunneling Spectroscopy (STS) in magnetic field up to 3 Tesla. Single gap conductance spectra due to c-axis tunneling were extensively measured, probing different amplitudes of the three-dimensional $\Delta_\pi$ as a function of Al content. Temperature and magnetic field dependences of the conductance spectra were studied in S-I-N configuration: the effect of the doping resulted in a monotonous reduction of the locally measured $T_C$ down to 24K for x=0.2. On the other hand, we have found that the gap amplitude shows a maximum value $\Delta_\pi= 2.3$ …